| HS Code | 174184 |
| Density | 1.24 g/cm³ |
| Water Absorption | 0.10% |
| Linear Mold Shrinkage | 0.0040 cm/cm |
| Melt Flow Rate | 10 g/10 min |
| Tensile Strength At Yield | 43.0 MPa |
| Tensile Strength At Break | 40.0 MPa |
| Elongation At Break | 10% |
| Tensile Modulus | 2.50 GPa |
| Flexural Strength | 70.0 MPa |
| Flexural Modulus | 2.80 GPa |
| Notched Izod Impact Strength | 0.400 J/cm |
| Unnotched Izod Impact Strength | 1.00 J/cm |
| Heat Deflection Temperature At 0 45 Mpa | 100 °C |
| Heat Deflection Temperature At 1 82 Mpa | 55 °C |
| Vicat Softening Temperature | 110 °C |
| Melting Temperature | 170 °C |
| Glass Transition Temperature | 60 °C |
| Processing Temperature | 210-230 °C |
| Mold Temperature | 25-50 °C |
| Drying Temperature | 80 °C |
| Drying Time | 4 hours |
| Filament Diameter | 1.75 mm |
| Color | Natural |
As an accredited Terraloy™ 3D-40040 Series High Impact/High Heat 3D Printing Polylactic Acid factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Terraloy™ 3D-40040 Series High Impact/High Heat 3D Printing Polylactic Acid comes in sealed 1 kg moisture-barrier foil bags. |
| Container Loading (20′ FCL) | 20′ FCL loaded with palletized Terraloy™ 3D-40040 high-impact/high-heat PLA pellets; moisture-barrier-wrapped bags/drums secured for safe ocean shipment. |
| Shipping | Terraloy™ 3D-40040 Series PLA is not classified as dangerous goods for transport by DOT, IMDG, IATA/ICAO, ADR/RID, or TDG. No UN number, proper shipping name, hazard class, or packing group assigned. Ship in sealed, labeled containers; keep dry, protect from moisture and heat, and follow local regulations. |
| Storage | Store Terraloy™ 3D-40040 Series High Impact/High Heat 3D Printing Polylactic Acid in a cool, dry, well-ventilated area. Keep sealed in original packaging or an airtight container with desiccant to prevent moisture uptake. Protect from direct sunlight, heat, sparks, and open flames. Avoid humid conditions. Maintain recommended storage temperature, typically 15–25°C. Use first-in, first-out stock rotation and reseal after each use. |
| Shelf Life | Shelf life: approximately 12 months when stored unopened in original packaging, cool, dry, and away from moisture, heat, and sunlight. |
Competitive Terraloy™ 3D-40040 Series High Impact/High Heat 3D Printing Polylactic Acid prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!