| HS Code | 238944 |
| Product Name | Stratasys Rigur Rubber-Like PolyJet 3D Printing Polymer Combination: Primary: TANGOGRAY FLX950; Secondary: TANGOBLACK FLX973 |
| Material Type | PolyJet Photopolymer |
| Technology | PolyJet 3D Printing |
| Primary Material | TangoGray FLX950 |
| Secondary Material | TangoBlack FLX973 |
| Color | Gray to Black (depending on mix ratio) |
| Shore A Hardness | Variable, typically 27-75 depending on mix ratio |
| Tensile Strength | Variable, typically 1.5-3.0 MPa |
| Elongation At Break | Variable, typically 100-220% |
| Tear Resistance | Variable, typically 4-7 kg/cm |
| Tensile Modulus | Variable, typically 0.8-2.5 MPa |
| Density | Approximately 1.13-1.14 g/cm³ |
| Water Absorption | Approximately 1.5% |
| Heat Deflection Temperature | Variable, typically 40-45°C |
| Vicat Softening Temperature | Variable, typically 45-50°C |
| Compressive Strength | Variable, typically 1.5-3.0 MPa |
| Flexural Modulus | Variable, typically 10-20 MPa |
As an accredited Stratasys Rigur Rubber-Like PolyJet 3D Printing Polymer Combination: Primary: TANGOGRAY FLX950; Secondary: TANGOBLACK FLX973 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Stratasys Rigur Rubber-Like PolyJet 3D Printing Polymer Combination: Primary: TANGOGRAY FLX950; Secondary: TANGOBLACK FLX973 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!