| HS Code | 114555 |
| Material Type | PLA Homopolymer |
| Form | Pellets |
| Density | 1.24 g/cm³ |
| Melt Flow Rate 190 C 2 16 Kg | 10.5 g/10 min |
| Glass Transition Temperature | 55-60°C |
| Melting Temperature | 170-180°C |
| Heat Deflection Temperature 0 45 Mpa | 120°C |
| Vicat Softening Point | 150°C |
| Tensile Strength At Yield | 70 MPa |
| Tensile Elongation At Break | 3% |
| Flexural Strength | 110 MPa |
| Flexural Modulus | 3600 MPa |
| Notched Izod Impact Strength | 2.5 kJ/m² |
| Rockwell Hardness | 88 R-scale |
| Biobased Content | 100% |
| Crystallinity | 35-45% |
| Stereochemical Purity | >99% L-isomer |
| Molecular Weight | 100,000 g/mol |
| Moisture Content | <0.025% |
| Drying Temperature | 80°C |
| Drying Time | 4 hours |
| Processing Temperature | 190-220°C |
| Mold Temperature | 100-120°C |
As an accredited PURAPOL L105 High Heat High Flow PLA Homopolymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | PURAPOL L105 High Heat High Flow PLA Homopolymer is supplied in 25 kg moisture-barrier foil-lined bags, palletized for bulk shipment. |
| Container Loading (20′ FCL) | Container Loading (20′ FCL): PURAPOL L105 High Heat High Flow PLA Homopolymer, palletized, shrink-wrapped, strapped, moisture-protected, evenly distributed, secure dunnage. |
| Shipping | PURAPOL L105 High Heat High Flow PLA Homopolymer ships as a nonhazardous solid polymer resin. Pack in sealed moisture-barrier bags or drums with desiccant. Transport in clean, dry vehicles at 15–25°C, away from heat, moisture, and direct sunlight. Label with product name, lot, and handling information. |
| Storage | Store PURAPOL L105 High Heat High Flow PLA Homopolymer in a cool, dry, well-ventilated area away from direct sunlight, heat, ignition sources, and moisture. Keep original containers tightly closed, upright, and palletized. Avoid prolonged storage above 30°C and protect from humid conditions to prevent hydrolytic degradation. Ensure good ventilation, avoid dust accumulation, and practice first-in, first-out stock rotation. |
| Shelf Life | Shelf life is 12 months from manufacture when stored unopened in original packaging, cool, dry, below 30°C, away from sunlight. |
Competitive PURAPOL L105 High Heat High Flow PLA Homopolymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!