HS Code |
597665 |
| Product Name | Polyethylene PE-L M2320 (DNDA-8320) |
| Type | Low Density Polyethylene (LDPE) |
| Melt Flow Index | 2.0 g/10min (190°C/2.16kg) |
| Density | 0.923 g/cm³ |
| Tensile Strength At Yield | 10 MPa |
| Elongation At Break | 400% |
| Flexural Modulus | 180 MPa |
| Vicat Softening Point | 93°C |
| Escr Condition A 100hr | Pass |
| Haze | 7% |
| Film Thickness Range | 20-200 microns |
| Application | Film extrusion |
| Processing Method | Blown film, Cast film |
| Impact Strength | Strong |
As an accredited Polyethylene PE-L M2320 (DNDA-8320) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Polyethylene PE-L M2320 (DNDA-8320) is packaged in 25 kg moisture-resistant, multi-layered polyethylene bags, labeled with product and safety information. |
| Shipping | Polyethylene PE-L M2320 (DNDA-8320) is shipped in moisture-proof, sealed 25 kg bags or bulk containers to prevent contamination. Store and transport in a cool, dry area, away from direct sunlight and incompatible substances. Ensure proper labeling and follow local regulations for chemical handling and transportation. |
| Storage | Polyethylene PE-L M2320 (DNDA-8320) should be stored in a cool, dry, well-ventilated area, away from direct sunlight, heat sources, and incompatible materials. Keep the product in its original, tightly sealed packaging to prevent contamination. Store away from strong oxidizing agents and ensure good housekeeping practices to minimize dust formation and accidental spills. Avoid exposure to temperatures above 40°C. |
Competitive Polyethylene PE-L M2320 (DNDA-8320) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615365186327 or mail to sales3@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615365186327
Email: sales3@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!