| HS Code | 916055 |
| Material | Polylactic Acid (PLA) |
| Film Types | Biaxially Oriented, Cast, Shrink |
| Biaxially Oriented Film Thickness | 10-50 µm |
| Cast Film Thickness | 20-100 µm |
| Shrink Film Thickness | 15-80 µm |
| Density | 1.24-1.25 g/cm³ |
| Tensile Strength Md | 40-150 MPa |
| Tensile Strength Td | 40-150 MPa |
| Elongation At Break | 2-100% depending on orientation |
| Tear Strength | 20-50 N/mm |
| Haze | 1-10% |
| Gloss | 80-100 GU |
| Light Transmittance | 90-95% |
| Glass Transition Temperature | 55-60°C |
| Melting Point | 150-170°C |
| Heat Seal Temperature | 80-120°C |
| Shrinkage At 80 C | 10-70% depending on shrink grade |
| Water Vapor Transmission Rate | 200-500 g/m²/day |
| Oxygen Transmission Rate | 500-2000 cm³/m²/day/atm |
| Carbon Dioxide Transmission Rate | 2000-5000 cm³/m²/day/atm |
| Biodegradability | Compostable under industrial conditions |
| Compostability | EN 13432, ASTM D6400 |
| Food Contact Compliance | FDA, EU 10/2011 |
| Printability | Good |
| Coefficient Of Friction | 0.2-0.4 |
| Surface Energy | 38-42 dyn/cm |
| Chemical Resistance | Good to oils; limited to strong acids and alkalis |
| Uv Resistance | Moderate |
| Storage Temperature | 10-30°C |
| Storage Humidity | 30-60% RH |
| Color | Transparent or custom |
| Surface Finish | Gloss or matte |
| Roll Width | 200-2000 mm |
| Roll Length | 1000-6000 m |
| Core Diameter | 76 mm or 152 mm |
As an accredited PLA film Biaxially Oriented/Cast/Shrink Film Polylactic Acid factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Supplied as 50 kg rolls; each PLA biaxially oriented/cast/shrink film roll is moisture-barrier wrapped and palletized for shipping. |
| Container Loading (20′ FCL) | 20′ FCL loading of PLA film (biaxially oriented, cast, or shrink) on pallets/rolls, securely stowed and moisture-protected for ocean transport. |
| Shipping | Shipping description: PLA film (biaxially oriented, cast, or shrink), polylactic acid; non-hazardous, not regulated for transport. Pack in dry, sealed, clean containers, protected from moisture, heat, and sunlight. No UN number, hazard class, or marine pollutant. Store at moderate temperatures; avoid puncture or crushing. |
| Storage | Store PLA film in a cool, dry, well-ventilated area away from direct sunlight, heat, ignition sources, and moisture. Keep in original sealed packaging to prevent hydrolysis and degradation. Avoid contact with strong acids, bases, solvents, and oxidizing agents. Maintain moderate temperature and low humidity; do not crush or stack excessively. Shelf life may be reduced by heat or moisture. |
| Shelf Life | PLA films typically have 12–24 months shelf life when sealed, cool, dry, UV-protected; heat and moisture accelerate hydrolysis/degradation. |
Competitive PLA film Biaxially Oriented/Cast/Shrink Film Polylactic Acid prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!