| HS Code | 379013 |
| Product Name | Mitsubishi FGF Recycled ABS-X 3D Printing Polymer |
| Material | Recycled ABS-X |
| Recycled Content | 100% |
| Form | Pellets |
| Color | Black |
| Density | 1.04 g/cm³ |
| Melt Flow Rate | 12 g/10 min (220 °C/10 kg) |
| Tensile Strength | 43 MPa |
| Tensile Modulus | 2100 MPa |
| Elongation At Break | 20% |
| Flexural Strength | 70 MPa |
| Flexural Modulus | 2000 MPa |
| Notched Izod Impact Strength | 20 kJ/m² |
| Heat Deflection Temperature | 90 °C at 1.8 MPa |
| Vicat Softening Temperature | 105 °C |
| Glass Transition Temperature | 105 °C |
| Processing Temperature | 250-270 °C |
| Bed Temperature | 100-110 °C |
| Drying Temperature | 80 °C |
| Drying Time | 4 h |
| Shrinkage | 0.4-0.6% |
| Water Absorption | 0.2% |
| Chemical Resistance | Good against acids, alkalis, alcohols, and oils |
As an accredited Mitsubishi FGF Recycled ABS-X 3D Printing Polymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Mitsubishi FGF Recycled ABS-X 3D Printing Polymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!