| HS Code | 288287 |
| Material | Mitsubishi FGF PP Glassfiber (30%) |
| Polymer Type | Polypropylene (PP) |
| Glass Fiber Content | 30% |
| Density | 1.12 g/cm3 |
| Tensile Strength | 80 MPa |
| Tensile Modulus | 6000 MPa |
| Elongation At Break | 3% |
| Flexural Modulus | 5500 MPa |
| Flexural Strength | 110 MPa |
| Notched Izod Impact Strength | 10 kJ/m2 |
| Heat Deflection Temperature At 0 45 Mpa | 150 C |
| Heat Deflection Temperature At 1 82 Mpa | 100 C |
| Melting Point | 165 C |
| Water Absorption | 0.02% |
| Molding Shrinkage | 0.3-0.8% |
| Processing Technology | Fused Granulate Fabrication (FGF) |
| Nozzle Temperature | 230-260 C |
| Bed Temperature | 80-100 C |
As an accredited Mitsubishi FGF PP Glassfiber (30%) PP, 30% Glass Fiber Filled 3D Printing Polymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Mitsubishi FGF PP Glassfiber (30%) PP, 30% Glass Fiber Filled 3D Printing Polymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!