| HS Code | 587776 |
| Material Family | Polylactic acid (PLA) |
| Grade | PLA-X3 |
| Form | Pellets |
| Processing Method | Fused Granular Fabrication (FGF) |
| Density | 1.24 g/cm3 |
| Melt Flow Rate | 15 g/10 min at 190 C/2.16 kg |
| Tensile Strength | 55 MPa |
| Tensile Modulus | 3500 MPa |
| Elongation At Break | 5% |
| Flexural Strength | 85 MPa |
| Flexural Modulus | 3500 MPa |
| Notched Izod Impact Strength | 3 kJ/m2 |
| Heat Deflection Temperature | 55 C at 0.45 MPa |
| Vicat Softening Temperature | 60 C |
| Melting Temperature | 155 C |
| Glass Transition Temperature | 60 C |
| Printing Temperature | 190-220 C |
| Bed Temperature | 40-60 C |
| Biobased Content | >90% |
As an accredited Mitsubishi FGF PLA-X3 PLA 3D Printing Polymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Mitsubishi FGF PLA-X3 PLA 3D Printing Polymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!