| HS Code | 754289 |
| Matrix Polymer | PLA (Polylactic Acid) |
| Filler Material | Copper |
| Filler Content | 80% by weight |
| Form | Pellets |
| Recommended Process | Fused Granular Fabrication (FGF) |
| Color | Copper metallic |
| Density | Approx. 3.9-4.0 g/cm³ |
| Melt Flow Rate | Approx. 10-20 g/10 min (190°C/2.16 kg) |
| Tensile Strength | Approx. 15-25 MPa |
| Tensile Modulus | Approx. 4-8 GPa |
| Elongation At Break | Approx. 1-3% |
| Flexural Strength | Approx. 25-40 MPa |
| Flexural Modulus | Approx. 4-8 GPa |
| Notched Izod Impact Strength | Approx. 2-5 kJ/m² |
| Heat Deflection Temperature | Approx. 50-60°C |
| Thermal Conductivity | Approx. 1-3 W/m·K |
| Electrical Conductivity | Conductive (volume resistivity < 10^2 Ω·cm) |
| Printing Temperature | 190-220°C |
| Bed Temperature | 0-60°C |
| Nozzle Diameter | ≥0.6 mm |
| Drying Conditions | 40-50°C for 4-6 hours |
As an accredited Mitsubishi FGF PLA Copper PLA, 80% Copper Filled 3D Printing Polymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Mitsubishi FGF PLA Copper PLA, 80% Copper Filled 3D Printing Polymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!