| HS Code | 338555 |
| Density | 1.45 g/cm³ |
| Filler Type | Glass Fiber |
| Filler Content | 19% |
| Tensile Modulus | 6500 MPa |
| Tensile Strength | 85 MPa |
| Elongation At Break | 2.0% |
| Flexural Modulus | 6000 MPa |
| Flexural Strength | 130 MPa |
| Notched Izod Impact Strength | 6.0 kJ/m² |
| Notched Charpy Impact Strength | 6.0 kJ/m² |
| Heat Deflection Temperature At 1 82 Mpa | 90 °C |
| Heat Deflection Temperature At 0 45 Mpa | 105 °C |
| Vicat Softening Temperature | 95 °C |
| Glass Transition Temperature | 80 °C |
| Processing Temperature | 250–270 °C |
| Mold Temperature | 80–100 °C |
| Drying Temperature | 80 °C |
| Drying Time | 4–6 h |
| Moisture Content | 0.02% |
| Linear Mold Shrinkage | 0.3% |
| Water Absorption | 0.1% |
| Rockwell Hardness | M 95 |
As an accredited Mitsubishi FGF PIPG PET-G, 19% Glass Fiber Filled 3D Printing Polymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Mitsubishi FGF PIPG PET-G, 19% Glass Fiber Filled 3D Printing Polymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!