| HS Code | 465165 |
| Material Type | Polypropylene (PP) |
| Filler Type | Glass Fiber |
| Glass Fiber Content | 30% |
| Density | 1.12 g/cm³ |
| Tensile Strength | 80 MPa |
| Tensile Modulus | 5800 MPa |
| Elongation At Break | 3% |
| Flexural Strength | 120 MPa |
| Flexural Modulus | 5000 MPa |
| Charpy Notched Impact Strength | 6 kJ/m² |
| Heat Deflection Temperature At 0 45 Mpa | 150 °C |
| Heat Deflection Temperature At 1 8 Mpa | 100 °C |
| Vicat Softening Temperature | 150 °C |
| Melting Temperature | 165 °C |
| Water Absorption | 0.02% |
| Molding Shrinkage | 0.3-0.5% |
| Melt Flow Rate | 5 g/10 min |
| Print Temperature | 240-260 °C |
| Bed Temperature | 80-100 °C |
| Drying Temperature | 80 °C |
| Drying Time | 4 h |
As an accredited Mitsubishi FGF PIPG Glassfiber (30%) PP, 30% Glass Fiber Filled 3D Printing Polymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Mitsubishi FGF PIPG Glassfiber (30%) PP, 30% Glass Fiber Filled 3D Printing Polymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!