| HS Code | 556623 |
| Polymer Type | PET-G |
| Filler Type | Carbon Fiber |
| Carbon Fiber Content | 15% |
| Density | 1.35 g/cm³ |
| Tensile Strength | 55 MPa |
| Tensile Modulus | 6,000 MPa |
| Elongation At Break | 1.5% |
| Flexural Strength | 90 MPa |
| Flexural Modulus | 5,500 MPa |
| Notched Impact Strength | 4 kJ/m² |
| Heat Deflection Temperature At 0 45 Mpa | 75°C |
| Heat Deflection Temperature At 1 82 Mpa | 65°C |
| Glass Transition Temperature | 78°C |
| Printing Temperature | 240-270°C |
| Bed Temperature | 80-100°C |
| Drying Temperature | 65°C |
| Drying Time | 4-6 hours |
| Moisture Absorption | 0.2% |
As an accredited Mitsubishi FGF CARBON-P PET-G, 15% Carbon Fiber Filled 3D Printing Polymer factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Mitsubishi FGF CARBON-P PET-G, 15% Carbon Fiber Filled 3D Printing Polymer prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!