| HS Code | 905220 |
| Material Type | Polyamide High Temperature (PAHT) |
| Filler | Carbon Fiber |
| Color | Black |
| Density | 1.18 g/cm³ |
| Tensile Strength | 135 MPa |
| Tensile Modulus | 10000 MPa |
| Elongation At Break | 1.5% |
| Flexural Strength | 190 MPa |
| Flexural Modulus | 8500 MPa |
| Charpy Notched Impact Strength | 4 kJ/m² |
| Heat Deflection Temperature | 250 °C |
| Melting Temperature | 295 °C |
| Print Temperature | 290-310 °C |
| Bed Temperature | 100-120 °C |
| Filament Diameter | 1.75 mm |
As an accredited Lehvoss LUVOCOM 3F PAHT CF 9891 BK Nylon, Mineral Filled, for Additive Manufacturing factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | |
| Shipping | |
| Storage |
Competitive Lehvoss LUVOCOM 3F PAHT CF 9891 BK Nylon, Mineral Filled, for Additive Manufacturing prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!