| HS Code | 346445 |
| Material Type | Polylactic Acid (PLA) Bioresin Compound |
| Color | Natural |
| Density | Approx. 1.25 g/cm³ |
| Melt Flow Rate | 10-20 g/10 min (190°C/2.16 kg) |
| Tensile Strength | 50-60 MPa |
| Tensile Modulus | 3500 MPa |
| Elongation At Break | 3-5% |
| Flexural Modulus | 3500-4000 MPa |
| Flexural Strength | 70-80 MPa |
| Charpy Notched Impact Strength | 2-3 kJ/m² |
| Charpy Unnotched Impact Strength | 15-20 kJ/m² |
| Heat Deflection Temperature | 50-55°C at 0.45 MPa |
| Vicat Softening Temperature | 60°C |
| Melting Temperature | 150-170°C |
| Glass Transition Temperature | 55-60°C |
| Processing Temperature | 180-220°C |
| Mold Temperature | 20-60°C |
| Drying Temperature | 80°C |
| Drying Time | 4 h |
| Moisture Content | <0.025% |
| Molding Shrinkage | 0.3-0.6% |
| Bio Based Content | >95% |
| Biodegradability | Compostable according to EN 13432 |
As an accredited Latigea B01 NAT Bioresin Polylactic Acid Injection Molding Compound factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Packaged in 25 kg moisture-barrier foil bags, palletized and labeled Latigea B01 NAT Bioresin Polylactic Acid Injection Molding Compound. |
| Container Loading (20′ FCL) | Container Loading (20′ FCL): Latigea B01 NAT Bioresin Polylactic Acid Injection Molding Compound, palletized and shrink-wrapped for secure transport. |
| Shipping | Latigea B01 NAT Bioresin Polylactic Acid Injection Molding Compound ships as a non-hazardous, non-flammable solid. Package in sealed moisture-barrier bags or fiber drums. Store and transport dry at ambient temperature, away from heat, moisture, and direct sunlight. Not regulated by DOT, IATA, IMDG, or ADR. Handle as industrial raw material. |
| Storage | Store Latigea B01 NAT Bioresin Polylactic Acid Injection Molding Compound in a cool, dry, well-ventilated area away from direct sunlight, heat, and ignition sources. Keep containers tightly sealed to prevent moisture absorption. Avoid humid conditions; use desiccants if necessary. Maintain stable temperatures, preferably below 30°C, and follow supplier guidance on shelf life and drying before processing. |
| Shelf Life | Shelf life is typically 12 months when stored unopened in original packaging, cool and dry, away from moisture and sunlight. |
Competitive Latigea B01 NAT Bioresin Polylactic Acid Injection Molding Compound prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!