| HS Code | 954265 |
| Material Type | Cellulosic fiber reinforced polylactic acid (PLA) |
| Reinforcement | Cellulosic fiber |
| Density | Approximately 1.32 g/cm³ |
| Melt Flow Rate | Approximately 10-15 g/10 min at 190°C/2.16 kg |
| Tensile Strength | Approximately 55 MPa |
| Tensile Elongation At Break | Approximately 2-3% |
| Flexural Strength | Approximately 85 MPa |
| Flexural Modulus | Approximately 4.0-4.5 GPa |
| Notched Izod Impact Strength | Approximately 3 kJ/m² |
| Heat Deflection Temperature | Approximately 120°C at 0.45 MPa |
| Vicat Softening Point | Approximately 120°C |
| Melting Point | Approximately 170°C |
| Glass Transition Temperature | Approximately 60°C |
| Mold Shrinkage | Approximately 0.3-0.6% |
| Water Absorption | Approximately 0.2-0.5% |
| Biobased Content | Approximately 100% |
| Rockwell Hardness | Approximately R110 |
| Processing Temperature | Approximately 190-210°C |
| Mold Temperature | Approximately 20-40°C |
| Drying Conditions | Approximately 80°C for 4 hours |
As an accredited FC 32130 Cellulosic Fiber Reinforced Injection Molding Polylactic Acid factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | FC 32130 Cellulosic Fiber Reinforced Injection Molding Polylactic Acid supplied in 25 kg moisture-barrier bags, palletized, stretch-wrapped for shipment. |
| Container Loading (20′ FCL) | 20′ FCL container loaded with FC 32130 Cellulosic Fiber Reinforced Injection Molding Polylactic Acid, securely palletized, dry conditions, standard handling. |
| Shipping | Shipping: FC 32130 Cellulosic Fiber Reinforced Injection Molding Polylactic Acid is generally transported as a non-dangerous, solid polymer in sealed moisture-barrier bags, drums, or octabins. Keep cool, dry, and away from ignition sources. Follow applicable transport regulations and consult the SDS for handling and emergency guidance. |
| Storage | Store FC 32130 Cellulosic Fiber Reinforced Injection Molding Polylactic Acid in sealed, moisture-barrier containers in a cool, dry, well-ventilated area. Protect from heat, direct sunlight, moisture, and ignition sources. Keep away from incompatible chemicals, oxidizers, and dust. Maintain stable ambient temperature, prevent moisture absorption, inspect containers periodically, and follow SDS. Use first-in, first-out stock rotation. |
| Shelf Life | Store unopened in a cool, dry place; typical shelf life is 12 months. Protect from moisture, heat, and direct sunlight. |
Competitive FC 32130 Cellulosic Fiber Reinforced Injection Molding Polylactic Acid prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!