| HS Code | 373568 |
| Material Type | Polylactic Acid (PLA) |
| Reinforcement Type | Short Fiber |
| Reinforcement Content | 30% |
| Processing Method | Injection Molding |
| Density | 1.42 g/cm³ |
| Melt Flow Rate | 10 g/10 min (190°C/2.16 kg) |
| Tensile Strength At Break | 85 MPa |
| Tensile Elongation At Break | 2.5% |
| Tensile Modulus | 8000 MPa |
| Flexural Modulus | 7500 MPa |
| Flexural Strength | 130 MPa |
| Notched Izod Impact Strength | 55 J/m |
| Unnotched Izod Impact Strength | 300 J/m |
| Heat Deflection Temperature At 1 8 Mpa | 140 °C |
| Heat Deflection Temperature At 0 45 Mpa | 155 °C |
| Vicat Softening Point | 150 °C |
| Mold Shrinkage Flow | 0.2% |
| Mold Shrinkage Cross Flow | 0.4% |
| Water Absorption | 0.2% |
| Processing Melt Temperature | 190-220 °C |
| Mold Temperature | 25-60 °C |
| Drying Temperature | 80 °C |
| Drying Time | 4 h |
As an accredited FC 10130 Short Fiber Reinforced Injection Molding Polylactic Acid factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | FC 10130 Short Fiber Reinforced Injection Molding Polylactic Acid supplied in 25 kg moisture-proof paper bags, palletized for industrial shipping. |
| Container Loading (20′ FCL) | FC 10130 Short Fiber Reinforced Injection Molding Polylactic Acid is palletized and securely loaded into a 20′ FCL container for shipment. |
| Shipping | FC 10130 Short Fiber Reinforced Injection Molding Polylactic Acid is typically shipped as non-hazardous, moisture-sensitive polymer pellets in sealed, lined bags or drums. It is not classified as dangerous goods for transport. Store cool, dry, away from heat and moisture. Protect packaging from rupture and contamination during handling and follow local regulations. |
| Storage | Store in a cool, dry, well-ventilated area away from direct sunlight, heat, ignition sources, and strong oxidizers. Keep original containers tightly sealed to prevent moisture absorption, which can degrade polylactic acid. Avoid dust generation and static discharge. Maintain ambient temperature, ideal below 30°C, with low humidity. Use clean, dry handling equipment and follow local regulations for combustible organic polymer powders/pellets. |
| Shelf Life | Shelf life typically 12 months when stored unopened in a cool, dry place, protected from moisture, heat, and direct sunlight. |
Competitive FC 10130 Short Fiber Reinforced Injection Molding Polylactic Acid prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618136850665 or mail to admin@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618136850665
Email: admin@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!