| HS Code | 660589 |
| Polymer Type | Ultra-high molecular weight polyethylene (UHMW-PE) |
| Density | 0.930 g/cm³ |
| Molecular Weight | 2.0 × 10^6 g/mol |
| Bulk Density | 0.40 g/cm³ |
| Average Particle Size | 150 µm |
| Tensile Strength At Yield | 17 MPa |
| Tensile Strength At Break | 40 MPa |
| Tensile Modulus | 700 MPa |
| Elongation At Break | 350% |
| Charpy Notched Impact Strength | 100 kJ/m² |
| Hardness Shore D | 62 |
| Melting Point | 135 °C |
| Vicat Softening Point | 80 °C |
| Thermal Conductivity | 0.41 W/m·K |
| Coefficient Of Linear Thermal Expansion | 1.5 × 10^-4 /°C |
| Dielectric Constant | 2.3 |
| Volume Resistivity | 1 × 10^15 ohm·cm |
| Water Absorption | <0.01% |
As an accredited Celanese UHMW-PE 4014 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Celanese UHMW-PE 4014 is packaged in 25 kg net multiwall paper bags, palletized and shrink-wrapped. |
| Container Loading (20′ FCL) | 20′ FCL container loading of Celanese UHMW-PE 4014: palletized bags, stretch-wrapped, evenly distributed, braced, and secured for export shipment. |
| Shipping | Celanese UHMW-PE 4014 is a non-hazardous polyethylene resin. For shipment, it is not classified as dangerous goods under DOT, IMDG, IATA, or ADR. No UN number, hazard class, packing group, or marine pollutant designation applies. Transport in clean, dry, closed containers away from ignition sources. |
| Storage | Store Celanese UHMW-PE 4014 in its original packaging in a cool, dry, well-ventilated area. Keep away from heat, sparks, flames, direct sunlight, and strong oxidizers. Protect from moisture and contamination. Keep containers closed when not in use. Minimize dust generation; use grounding and bonding to prevent static discharge. Follow local regulations. |
| Shelf Life | Stable indefinitely under recommended storage conditions in original packaging; protect from moisture, direct sunlight, heat, and contamination. |
Celanese UHMW-PE 4014 is an ultra-high-molecular-weight polyethylene powder whose high melt viscosity requires processing routes that avoid conventional screw plastication. The application scenarios selected below are limited to industrial sectors with confirmed use of UHMW-PE; no adjacent or speculative downstream fields are included. Where published data for the 4014 grade are absent in a specific formulation, the text identifies that limitation instead of substituting unverifiable numerical claims. The compliance matrix below should be read together with the scenario paragraphs, because standard designations in the table are not repeated in every sentence.
| Application scenario | Compliance standard / regulation | Test method / designation | Parameter controlled |
|---|---|---|---|
| Wet-process lithium-ion separator film | IEC 62660-1:2018 | ASTM D882-18 / ISO 15901-1:2016 | MD/TD tensile strength, pore volume distribution |
| Gel-spun high-tenacity fibre | ASTM D7269-17 / ISO 2060:1994 / NIJ 0101.06 | Yarn tensile, linear density, ballistic panel test | Tenacity, modulus, denier |
| Neat wear segments by ram extrusion / compression moulding | FDA 21 CFR 177.1520 / EU Regulation 10/2011 | ASTM D4020-18 / ASTM D638-14 | Reduced inherent viscosity, tensile properties |
| Sintered porous media | ISO 16889:2022 / ISO 2941:2009 | ASTM E128-99(2019) / ISO 15901-1:2016 | Bubble point, pore diameter, burst pressure |
| PE100 pipe abrasion modification | ISO 4427-2:2019 / ASTM F714-21 | ASTM G75-15 | Hydrostatic design stress, slurry wear response |
| Lead-acid battery separator sheet | IEC 61056-1:2012 / DIN 40742 | ASTM D882-18 | Puncture resistance, basis weight, porosity |
In wet-process lithium-ion battery separator production, Celanese UHMW-PE 4014 is dry-blended with a lower-molecular-weight HDPE carrier and a high-boiling paraffin oil plasticiser; reported polymer-fraction loadings for UHMW-PE in this process are 10–30 wt%, although published data for the 4014 grade in a specific separator formulation are limited and the actual charge is controlled by the target puncture resistance and shutdown melt-integrity. The mixture is fed into a co-rotating twin-screw extruder with L/D 40:1 or longer, and the paraffin oil is injected downstream of the polymer melting zone at a barrel section where the screw channel is partially filled; this injection point is used to limit torque demand and prevent the high-viscosity melt from overheating above 210 °C. The resulting gel is cast through a coat-hanger T-die at 190–210 °C, cooled on a chilled roll to a gel sheet, and biaxially stretched at 90–130 °C; the paraffin oil is then extracted with n-heptane or dichloromethane in a counter-current solvent bath, followed by heat-setting at 120–135 °C under controlled tension. Separator compliance in battery plants is verified against IEC 62660-1:2018 for mechanical abuse during cell qualification, while film-level tensile and porosity are measured under ASTM D882-18 and ISO 15901-1:2016, respectively, with Gurley densometer values typically controlled below 300 s/100 mL for high-rate cylindrical cells. The terminal article is a single-layer or multilayer microporous separator for lithium-ion secondary cells; the UHMW-PE fraction contributes to melt-integrity at elevated temperature and to puncture resistance during nail penetration, but it also raises the gel viscosity, so the addition level cannot be increased without reducing casting line speed or raising solvent-extraction load.
Gel spinning of Celanese UHMW-PE 4014 requires forming a solution with a non-volatile solvent such as decalin or white mineral oil at solids concentrations between 3 wt% and 10 wt%; the lower end of this range is used when spinneret pressure is governed by the high molecular weight fraction, while the upper end improves throughput but demands higher filtration pressure and longer dissolution residence time. The solution is prepared in a heated horizontal kneader or in a co-rotating twin-screw dissolving unit at 150–180 °C, then metered by a gear pump through a spinneret with capillary diameters from 0.5 mm to 1.5 mm and L/D ratios near 10:1. Filtration behind the spinneret is normally specified at 20–50 μm mesh; the pressure rise across this pack is the main indicator of undissolved gel particles and defines the maximum continuous spinning campaign before pack replacement. The extruded gel fibre is quenched in air or water, drawn in a first stage at ratios between 1:3 and 1:10, solvent-extracted with n-heptane or dichloromethane, and hot-drawn at 130–150 °C to total draw ratios up to 1:80. Fibre compliance is anchored to ASTM D7269-17 for tensile strength and modulus of UHMW-PE yarns, ISO 2060:1994 for linear density, and NIJ 0101.06 for ballistic panel qualification when the yarn is converted into fabric. The terminal articles are ballistic-resistant soft armour panels, high-modulus marine ropes, and cut-resistant gloves; industrial acceptance for high-tenacity UHMW-PE yarns is commonly set at tenacity values above 30 cN/dtex under ASTM D7269-17. Celanese UHMW-PE 4014 may be sieved to a particle size below 150 μm before dissolution to reduce gel specks, but published data specific to this grade in gel spinning are limited, so the sieving specification is established on a lot-by-lot basis.
For neat wear segments, Celanese UHMW-PE 4014 is processed directly from the powder state by compression moulding or ram extrusion because the high melt viscosity prevents screw plastication; when colouring or lubrication is required, a carbon black masterbatch is added at 0.5–2.0 wt%, and published data for other additives specific to 4014 are limited. Compression moulding is performed at platen temperatures of 190–220 °C and pressures of 10–20 MPa, with hold time scaled at approximately 10–15 min per 25 mm of section thickness and cooling under pressure at 5–10 °C/min to control planar flatness. Ram extrusion uses a reciprocating press with barrel zones held at 180–200 °C and die land temperatures at 170–190 °C, followed by controlled water-bath cooling; the ram stroke speed is limited by the rate of heat conduction through the powder column, which is the primary bottleneck for thick sections above 50 mm. Compliance for food-contact components is verified under FDA 21 CFR 177.1520 and EU Regulation 10/2011; mechanical property verification references ASTM D4020-18 for reduced inherent viscosity to confirm molecular weight retention after processing and ASTM D638-14 for tensile properties. Terminal articles machined from these stock shapes include conveyor wear strips, chain guides, star wheels, and guide rails for bottling, packaging, and material-handling lines. The process window is narrow at the upper platen temperature: prolonged exposure above 220 °C can cause oxidation-related yellowing and a measurable drop in reduced inherent viscosity, while insufficient temperature below 190 °C produces incomplete particle coalescence and internal voids.
Porous sintered articles from Celanese UHMW-PE 4014 are produced by heating the powder in a closed mould to a point below complete melt flow, so the as-supplied particle size distribution controls the pore morphology; the addition level of any sacrificial binder is 0 wt%, and for filtration grades the powder is normally sieved to 100–300 μm. The mould is heated to 175–200 °C at a maximum heating rate of 2 °C/min, held for 20–40 min depending on part thickness, and cooled under pressure at 3–8 °C/min to prevent warpage. Compliance for industrial filter elements references ISO 16889:2022 for filtration performance and ISO 2941:2009 for collapse/burst resistance; for food-contact porous media, FDA 21 CFR 177.1520 applies. Terminal articles include wastewater aeration diffusers, gas venting plugs, and dust collection cartridges. Because published data for the bubble point and pore size distribution of 4014 sintered parts are limited, the pore size is verified on each tooling set by ASTM E128-99(2019) bubble-point porometry or mercury intrusion under ISO 15901-1:2016. Sintering temperature is the critical control variable: a thermal overshoot above 200 °C can collapse the pore network by driving the powder into full melting, while failure to reach 175 °C yields weak neck formation and low burst pressure.
In PE100 pressure pipe compounds for mining slurry and dredging service, Celanese UHMW-PE 4014 is dosed into the feed throat at 1–3 wt% of the total formulation; addition above 5 wt% is not recommended because the high melt viscosity of UHMW-PE produces dispersion defects, increases melt pressure at the screen pack, and can reduce the smoothness of the pipe bore. The compound is processed in a co-rotating twin-screw extruder with L/D 40:1 and distributive mixing elements, followed by underwater pelletizing and subsequent pipe extrusion at melt temperatures between 200 °C and 230 °C. Compliance for the finished pipe is referenced to ISO 4427-2:2019 for PE100 piping, ASTM F714-21 for outside-diameter-controlled HDPE pipe, and slurry abrasion response is assessed under ASTM G75-15. Terminal articles are solid-wall HDPE pipes, dredge floats, and slurry transport spools where the UHMW-PE addition is specified to improve bore wear resistance under wet particulate flow. Published data for the exact wear improvement provided by 4014 at this loading are limited; comparative slurry abrasion testing must be run on each lot against a control PE100 compound, because the dispersibility of the high-molar-mass grade can vary with batch particle size and feed moisture.
For lead-acid battery separator sheet, Celanese UHMW-PE 4014 is compounded with precipitated silica and a lower-density polyethylene carrier at an UHMW-PE addition level of 5–12 wt% of the total compound, with silica typically 50–60 wt% and the balance PE; the exact formulation is adjusted to achieve the target puncture resistance and porosity while retaining envelope-sealing behaviour. The blend is mixed in an internal mixer or twin-screw extruder at 180–210 °C, calendered into sheet, and the plasticising oil is extracted with a solvent to create micropores; the sheet is then dried, slit, and formed into envelope separators. Compliance is governed by IEC 61056-1:2012 for lead-acid battery separators, with puncture resistance and basis weight verified under DIN 40742 or ASTM D882-18. Terminal products are envelope separators for SLI automotive and industrial lead-acid cells. Published data for the specific silica dispersion quality achieved with 4014 in this process are limited, so the mixing energy and oil-extraction line speed are established on pilot-scale equipment before full production release.
Competitive Celanese UHMW-PE 4014 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8618005193850 or mail to sales8@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8618005193850
Email: sales8@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!
Celanese UHMW-PE 4014 is a virgin ultra-high-molecular-weight polyethylene resin in the GUR 4000 series. The grade is specified primarily by dilute-solution viscosity rather than melt flow rate, because the molar mass produces a melt viscosity that is not practically measurable under standard melt flow protocols. Typical lot release data include a density of 0.930 g/cm³ by ISO 1183-1, a bulk density of 0.45 g/cm³ by ISO 60, and a viscosity number of 2400 cm³/g by ISO 1628-3. The corresponding average molecular weight is reported as approximately 6.0 × 10⁶ g/mol when calculated from the viscosity-number correlation in ASTM D4020. The powder is normally converted by ram extrusion or compression molding; conventional single-screw extrusion is not suitable because the high entanglement density prevents stable melt pumping.
Lot acceptance for Celanese UHMW-PE 4014 is based on viscosity number, density, bulk density, particle-size distribution, and residual moisture rather than on melt flow rate. Under ISO 1133-1:2022, condition 190 °C/21.6 kg, the material exhibits a melt flow rate below the practical detection limit. This absence of measurable flow is a specification boundary separating UHMW-PE from conventional HDPE extrusion grades. The viscosity number is determined in decalin at 135 °C according to ISO 1628-3. A batch-to-batch shift of ±50 cm³/g around the published value is capable of altering ram pressure and final impact response in thick sections. Residual moisture is controlled because free moisture can form steam bubbles during compression molding at temperatures above 200 °C. Sieve residue and fines content are also monitored to maintain uniform mold filling and consistent compacted density.
During ram extrusion on a 120 t hydraulic press with a 65 mm barrel, the powder is compacted at ambient temperature and then advanced through a heated die. Barrel temperatures are typically maintained between 220 °C and 250 °C, with die temperatures up to 260 °C to minimize surface roughness. Ram pressure rises during the heating and melt-coalescence stage of each billet cycle; operators frequently record peak pressures in the range of 30 MPa to 60 MPa at the ram face for solid profiles, depending on cross-section and line speed. Cooling is staged after the die to bring the profile below the crystalline melting point of 133 °C before cutting. Published data for this specific configuration is limited, so pressure and temperature settings should be confirmed with tooling trials on the installed press.
Compression-molded plaques of 10 mm thickness are used for mechanical characterization after conditioning at 23 °C and 50 % relative humidity. The values in the table are typical for virgin GUR 4014 and are not specification limits; they reflect the high molar mass and high entanglement density of the grade.
| Property | Test method | Typical value |
|---|---|---|
| Density | ISO 1183-1 | 0.930 g/cm³ |
| Viscosity number | ISO 1628-3 | 2400 cm³/g |
| Tensile stress at yield | ISO 527-2 | 21 MPa |
| Elongation at break | ISO 527-2 | ≥300 % |
| Tensile modulus | ISO 527-2 | 680 MPa |
| Shore D hardness | ISO 868 | 63 |
| Notched Charpy impact | ISO 179-1/1eA | No break at 23 °C |
| Vicat softening temperature | ISO 306/A50 | 80 °C |
The notched Charpy value is reported as no break at 23 °C because the specimen deforms plastically without crack propagation under ISO 179-1/1eA. At cryogenic temperatures, impact response becomes more dependent on molding pressure and internal fusion quality. The Shore D hardness of 63 is lower than that of many filled engineering thermoplastics, but the grade combines this hardness with a low coefficient of friction and high abrasion resistance in wet slurry environments.
Celanese UHMW-PE 4014 is selected for wear strips, chain guides, chute liners, conveyor rollers, screw flights, press pads, and pump wear components where conventional HDPE exhibits excessive abrasive wear and where cast nylon may be limited by moisture uptake or part cost. In dry sliding against polished steel, the dynamic coefficient of friction may fall between 0.10 and 0.20, but these values are system-dependent and require verification with the specific steel roughness, load, and velocity. The material is not suitable for injection molding because the melt viscosity remains too high even at temperatures approaching degradation onset. Its conversion is restricted to compression molding, ram extrusion, and machining of stock shapes from molded or extruded blanks.
The grade inherits the broad chemical resistance of polyethylene to dilute acids, alkalis, and brine. However, aromatic hydrocarbons, chlorinated solvents, and strong oxidizing acids may swell or degrade the surface. Contact with oxidizing media above 60 °C should be qualified by immersion testing under the intended service concentration and temperature. Unstabilized UHMW-PE is also susceptible to UV-initiated oxidative embrittlement during prolonged outdoor exposure; components exposed to direct sunlight should be produced from a UV-stabilized version or evaluated by ISO 4892-2 accelerated weathering.
Within the GUR 4000 series, the principal distinction among grades is molar mass and the resulting melt viscosity. A lower-viscosity grade such as GUR 4012 processes at lower ram pressure and faster output in thin-wall profiles, but it may exhibit a lower abrasion index in sand-water slurry tests. A higher-viscosity grade such as GUR 4150 offers greater abrasion resistance and toughness but demands longer heating cycles and higher compaction tonnage. Celanese UHMW-PE 4014 occupies the middle-to-high molar mass position; it is specified where the balance between ram extrusion line speed and wear life favors a viscosity number near 2400 cm³/g. Compared with an HDPE extrusion grade having a measurable melt flow rate, the molecular weight of GUR 4014 is higher by roughly one to two orders of magnitude, which eliminates conventional melt processing and shifts it to non-screw forming methods.
The following matrix identifies the regulatory and standards framework relevant to the grade. Inclusion in the matrix does not constitute a regulatory certification for every lot. Users must obtain the current Celanese regulatory data sheet for the specific grade and intended jurisdiction.
| Standard or regulation | Relevance to Celanese UHMW-PE 4014 |
|---|---|
| ISO 11542-1 | Designation system for polyethylene ultra-high-molecular-weight molding and extrusion materials |
| FDA 21 CFR 177.1520 | Olefin polymers permitted for food-contact use when extractives and density limits are met; grade-specific confirmation required |
| EU Regulation (EU) No 10/2011 | Positive list and migration limit framework for plastics intended for food contact; compliance depends on additive package |
| RoHS Directive 2011/65/EU | Restricts lead, mercury, cadmium, hexavalent chromium, PBB, and PBDE; virgin polyethylene is typically compliant but supplier certification is required |
| REACH Regulation (EC) No 1907/2006 | Registration, evaluation, and authorization obligations; article producers rely on supplier substance data |
Because the material is supplied as a low-bulk-density powder, transfer systems must avoid severe fines segregation. Pneumatic conveying at high air velocity can generate fines that alter apparent density and cause charge variation in ram extrusion. Storage at ambient temperature in tightly closed containers is generally sufficient because moisture regain is low, but condensation on cold powder should be avoided before charging a heated mold. Rework of machined swarf is possible only when the swarf is free of cutting fluids and is blended back into virgin powder at controlled levels. Published data for the allowable rework fraction in this specific grade is limited, so production trials are required before establishing a release protocol for regrind-containing stock shapes.